Group 12, by modern IUPAC numbering, is a group of chemical elements in the periodic table. It includes zinc (Zn), cadmium (Cd), mercury (Hg), and copernicium (Cn). Formerly this group was named IIB (pronounced as "group two B", as the "II" is a Roman numeral) by CAS and old IUPAC system. The three group 12 elements that occur naturally are zinc, cadmium and mercury. They are all widely used in electric and electronic applications, as well as in various alloys. The first two members of the group share similar properties as they are solid metals under standard conditions. Mercury is the only metal that is known to be a liquid at room temperature – as copernicium's boiling point has not yet been measured accurately enough, it is not yet known whether it is a liquid or a gas under standard conditions. While zinc is very important in the biochemistry of living organisms, cadmium and mercury are both highly toxic. As copernicium does not occur in nature, it has to be synthesized in the laboratory. Due to their complete d-shell they are sometimes excluded from the transition metals.
Physical and atomic properties Like other groups of the periodic table, the members of group 12 show patterns in its electron configuration, especially the outermost shells, which result in trends in their chemical behavior:
The group 12 elements are all soft, diamagnetic, divalent metals. They have the lowest melting points among all transition metals. Zinc is bluish-white and lustrous, though most common commercial grades of the metal have a dull finish. Zinc is also referred to in nonscientific contexts as spelter. Cadmium is soft, malleable, ductile, and with a bluish-white color. Mercury is a liquid, heavy, silvery-white metal. It is the only common liquid metal at ordinary temperatures, and as compared to other metals, it is a poor conductor of heat, but a fair conductor of electricity. The table below is a summary of the key physical properties of the group 12 elements. The data for copernicium is based on relativistic density-functional theory simulations.
Zinc is somewhat less dense than iron and has a hexagonal crystal structure. The metal is hard and brittle at most temperatures but becomes malleable between 100 and 150 °C (212 and 302 °F). Above 210 °C (410 °F), the metal becomes brittle again and can be pulverized by beating. Zinc is a fair conductor of electricity. For a metal, zinc has relatively low melting (419.5 °C, 787.1 °F) and boiling points (907 °C, 1,665 °F). Cadmium is similar in many respects to zinc but forms complex compounds. Unlike other metals, cadmium is resistant to corrosion and as a result it is used as a protective layer when deposited on other metals. As a bulk metal, cadmium is insoluble in water and is not flammable; however, in its powdered form it may burn and release toxic fumes. Mercury has an exceptionally low melting temperature for a d-block metal. A complete explanation of this fact requires a deep excursion into quantum physics, but it can be summarized as follows: mercury has a unique electronic configuration where electrons fill up all the available 1s, 2s, 2p, 3s, 3p, 3d, 4s, 4p, 4d, 4f, 5s, 5p, 5d and 6s subshells. As such configuration strongly resists removal of an electron, mercury behaves similarly to noble gas elements, which form weak bonds and thus easily melting solids. The stability of the 6s shell is due to the presence of a filled 4f shell. An f shell poorly screens the nuclear charge that increases the attractive Coulomb interaction of the 6s shell and the nucleus (see lanthanide contraction). The absence of a filled inner f shell is the reason for the somewhat higher melting temperature of cadmium and zinc, although both these metals still melt easily and, in addition, have unusually low boiling points. Gold has atoms with one less 6s electron than mercury. Those electrons are more easily removed and are shared between the gold atoms forming relatively strong metallic bonds. Zinc, cadmium and mercury form a large range of alloys. Among the zinc containing ones, brass is an alloy of zinc and copper. Other metals long known to form binary alloys with zinc are aluminium, antimony, bismuth, gold, iron, lead, mercury, silver, tin, magnesium, cobalt, nickel, tellurium and sodium. While neither zinc nor zirconium are ferromagnetic, their alloy ZrZn2 exhibits ferromagnetism below 35 K. Cadmium is used in many kinds of solder and bearing alloys, due to a low coefficient of friction and fatigue resistance. It is also found in some of the lowest-melting alloys, such as Wood's metal. Because it is a liquid, mercury dissolves other metals and the alloys that are formed are called amalgams. For example, such amalgams are known with gold, zinc, sodium, and many other metals. Because iron is an exception, iron flasks have been traditionally used to trade mercury. Other metals that do not form amalgams with mercury include tantalum, tungsten and platinum. Sodium amalgam is a common reducing agent in organic synthesis, and is also used in high-pressure sodium lamps. Mercury readily combines with aluminium to form a mercury-aluminium amalgam when the two pure metals come into contact. Since the amalgam reacts with air to give aluminium oxide, small amounts of mercury corrode aluminium. For this reason, mercury is not allowed aboard an aircraft under most circumstances because of the risk of it forming an amalgam with exposed aluminium parts in the aircraft.
Chemistry Most of the chemistry has been observed only for the first three members of the group 12. The chemistry of copernicium is not well established and therefore the rest of the section deals only with zinc, cadmium and mercury.
… excerpt ends here. Continue reading the full article.