Cast iron is a class of iron–carbon alloys with a carbon content of more than 2% and silicon content around 1–3%. Its usefulness derives from its relatively low melting temperature. The alloying elements determine the form in which its carbon appears: white cast iron has its carbon combined into the iron carbide compound cementite, which is very hard, but brittle, as it allows cracks to pass straight through; grey cast iron has graphite flakes which deflect a passing crack and initiate countless new cracks as the material breaks, and ductile cast iron has spherical graphite "nodules" which stop the crack from further progressing. Carbon (C), ranging from 1.8 to 4% by weight, and silicon (Si), 1–3% by weight, are the main alloying elements of cast iron. Iron alloys with lower carbon content are known as steel. Cast iron tends to be brittle, except for malleable cast irons. With its relatively low melting point, good fluidity, castability, excellent machinability, resistance to deformation and wear resistance, cast irons have become an engineering material with a wide range of applications and are used in pipes, machines and automotive industry parts, such as cylinder heads, cylinder blocks and gearbox cases. Some alloys are resistant to damage by oxidation. In general, cast iron is notoriously difficult to weld. The earliest cast-iron artifacts date to the 8th century BC, and were discovered by archaeologists in what is now Jiangsu, China. Cast iron was used in ancient China to mass-produce weaponry for warfare, as well as agriculture and architecture. During the 15th century AD, cast iron was utilized for cannons and shot in Burgundy, France, and in England during the Reformation. The amounts of cast iron used for cannons required large-scale production. The first cast-iron bridge was built during the 1770s by Abraham Darby III, and is known as the Iron Bridge in Shropshire, England. Cast iron was also used in the construction of buildings.
Production Cast iron is made from pig iron, which is the product of melting iron ore in a blast furnace. Cast iron can be made directly from the molten pig iron or by re-melting pig iron, often along with substantial quantities of iron, steel, limestone, carbon (coke) and taking various steps to remove undesirable contaminants. Phosphorus and sulfur may be burnt out of the molten iron, but this also burns out the carbon, which must be replaced. Depending on the application, carbon and silicon content are adjusted to the desired levels, which may be anywhere from 2–3.5% and 1–3%, respectively. If desired, other elements are then added to the melt before the final form is produced by casting.
Cast iron is sometimes melted in a special type of blast furnace known as a cupola, but in modern applications, it is more often melted in electric induction furnaces or electric arc furnaces. After melting is complete, the molten cast iron is poured into a holding furnace or ladle.
Types
Alloying elements
Cast iron's properties are changed by adding various alloying elements, or alloyants. Next to carbon, silicon is the most important alloyant because it forces carbon out of solution. A low percentage of silicon allows carbon to remain in solution, forming iron carbide and producing white cast iron. A high percentage of silicon forces carbon out of solution, forming graphite and producing grey cast iron. Other alloying agents, manganese, chromium, molybdenum, titanium, and vanadium counteract silicon, and promote the retention of carbon and the formation of those carbides. Nickel and copper increase strength and machinability, but do not change the amount of graphite formed. Carbon as graphite produces a softer iron, reduces shrinkage, lowers strength, and decreases density. Sulfur, largely a contaminant when present, forms iron sulfide, which prevents the formation of graphite and increases hardness. Sulfur makes molten cast iron viscous, which causes defects. To counter the effects of sulfur, manganese is added, because the two form into manganese sulfide instead of iron sulfide. The manganese sulfide is lighter than the melt, so it tends to float out of the melt and into the slag. The amount of manganese required to neutralize sulfur is 1.7 × sulfur content + 0.3%. If more than this amount of manganese is added, then manganese carbide forms, which increases hardness and chilling, except in grey iron, where up to 1% of manganese increases strength and density. Nickel is one of the most common alloying elements, because it refines the pearlite and graphite structures, improves toughness, and evens out hardness differences between section thicknesses. Chromium is added in small amounts to reduce free graphite, produce chill, and because it is a powerful carbide stabilizer; nickel is often added in conjunction. A small amount of tin can be added as a substitute for 0.5% chromium. Copper is added in the ladle or in the furnace, on the order of 0.5–2.5%, to decrease chill, refine graphite, and increase fluidity. Molybdenum is added on the order of 0.3–1% to increase chill and refine the graphite and pearlite structure; it is often added in conjunction with nickel, copper, and chromium to form high strength irons. Titanium is added as a degasser and deoxidizer, but it also increases fluidity. Vanadium at 0.15–0.5% is added to cast iron to stabilize cementite, increase hardness, and increase resistance to wear and heat. Zirconium at 0.1–0.3% helps to form graphite, deoxidize, and increase fluidity. In malleable iron melts, bismuth is added at 0.002–0.01% to increase how much silicon can be added. In white iron, boron is added to aid in the production of malleable iron; it also reduces the coarsening effect of bismuth.
Grey cast iron
… excerpt ends here. Continue reading the full article.